chemical characterisation:	oxidised LDPE wax
acid number [mg KOH/g]:	16
drop point [°C]:	102
density at 23°C [g/cm3]:	0.94
color/supply form:	almost white flakes*
main applications:	lubricant for PVC; water based emulsions
melt viscosity (at T) [mPa*s]:	800 (140°C)
penetration at 25°C [mm*10-¹]:	4
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised LDPE wax
acid number [mg KOH/g]:	14
drop point [°C]:	99
density at 23°C [g/cm3]:	0.94
color/supply form:	almost white flakes, *
main applications:	lubricant for PVC
melt viscosity (at T) [mPa*s]:	250 (140°C)
penetration at 25°C [mm*10-¹]:	6
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised LDPE wax
acid number [mg KOH/g]:	16
drop point [°C]:	100
density at 23°C [g/cm3]:	0.94
color/supply form:	almost white flakes, *
main applications:	lubricant for PVC; water based emulsions
melt viscosity (at T) [mPa*s]:	230 (140°C)
penetration at 25°C [mm*10-¹]:	6
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised PE wax
acid number [mg KOH/g]:	16
drop point [°C]:	104
density at 23°C [g/cm3]:	0.94
color/supply form:	almost white flakes, *
main applications:	lubricant for PVC; water based emulsions
melt viscosity (at T) [mPa*s]:	170 (140°C)
penetration at 25°C [mm*10-¹]:	3
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised PE wax
acid number [mg KOH/g]:	16
drop point [°C]:	102
density at 23°C [g/cm3]:	0.94
color/supply form:	almost white flakes, *
main applications:	lubricant for PVC; water based emulsions
melt viscosity (at T) [mPa*s]:	110 (140°C)
penetration at 25°C [mm*10-¹]:	3
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised synthetic wax
acid number [mg KOH/g]:	30
drop point [°C]:	103
density at 23°C [g/cm3]:	0.96
color/supply form:	almost white flakes*
main applications:	water based emulsions; eg. for release agent
melt viscosity (at T) [mPa*s]:	20 (120°C)
penetration at 25°C [mm*10-¹]:	4
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised polyolefin
acid number [mg KOH/g]:	7
drop point [°C]:	135 (DSC)
density at 23°C [g/cm3]:	0.98
color/supply form:	white powder
main applications:	fusion control and metal release in PVC appliations
melt viscosity (at T) [mPa*s]:	26000 (170°C)
penetration at 25°C [mm*10-¹]:	< 1
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume:

chemical characterisation:	oxidised polyolefin
acid number [mg KOH/g]:	16
drop point [°C]:	135 (DSC)
density at 23°C [g/cm3]:	0.98
color/supply form:	white powder
main applications:	fusion control and metal release in PVC appliations; water based emulsions
melt viscosity (at T) [mPa*s]:	8000 (160°C)
penetration at 25°C [mm*10-¹]:	< 1
wax for manufacturing of wax emulsions:
lubricant in PVC:
fusion promotion in PVC:
modifications of hot melts:
modifications of bitume: