Compatibiliser for glass fibre reinforced plastics

chemical characterisation:	maleic acid anhydride grafted wax
acid number [mg KOH/g]:	30
drop point [°C]:	108
density at 23°C [g/cm3]:	0.97
color/supply form:	almost white flakes*
main applications:	wetting and compatibilising of wood fibres
melt viscosity (at T) [mPa*s]:	40 (120°C)
penetration at 25°C [mm*10-¹]:	< 1
compatabiliser for glass fibre reinforced plastic:
flow & release additives for plastic processing:
texturing additives for powder coatings:
dispersing agents in color and additives masterbatches:
nucleating agents for plastics:

chemical characterisation:	maleic acid anhydride grafted PE wax
acid number [mg KOH/g]:	30
drop point [°C]:	112
density at 23°C [g/cm3]:	0.96
color/supply form:	almost white flakes*
main applications:	coupling agent for fibres / fillers in PE and PVC based WPC, hot melt, water based emulsions
melt viscosity (at T) [mPa*s]:	150 (120°C)
penetration at 25°C [mm*10-¹]:	< 1
compatabiliser for glass fibre reinforced plastic:
flow & release additives for plastic processing:
texturing additives for powder coatings:
dispersing agents in color and additives masterbatches:
nucleating agents for plastics:

chemical characterisation:	maleic acid anhydride grafted PP wax
acid number [mg KOH/g]:	40
drop point [°C]:	152
density at 23°C [g/cm3]:	0.93
color/supply form:	pale yellowish flakes*
main applications:	coupling agent in glass fibre filled PP, compatibliser in PP based WPC
melt viscosity (at T) [mPa*s]:	800 (170°C)
penetration at 25°C [mm*10-¹]:	< 1
compatabiliser for glass fibre reinforced plastic:
flow & release additives for plastic processing:
texturing additives for powder coatings:
dispersing agents in color and additives masterbatches:
nucleating agents for plastics: